Thông số kỹ thuật
Description
APPC 1101 SC is a CR-modified propylene homopolymer for the production of spunbonded Nonwovens with high resistance to gas fading.
Application
Non wovens spun bonded.
Properties ( Typical values)
Properties | Unit | Test method | Value |
Melt Flow Rate | |||
Melt flow rate (230°C / 2.16 KG) |
g / 10 min |
ISO 1133 |
35.0 |
Mechnical Properties | |||
Tensile modulus of elasticity (v= 1 mm/min) |
MPa |
ISO 527-2 |
1450 |
Tensile yield at stress (v= 50 mm/min) |
MPa |
ISO 527-2 |
34 |
Tensile yield at strain (v= 50 mm/min) |
% |
ISO 527-2 |
8 |
Tensile strain at break (v= 50 mm/min) |
% |
ISO 527-2 |
>50 |
Charpy impact strength unnotched (+23°C) | kJ/m2 |
ISO 179/1eU |
100 |
Charpy impact strength notched (+23°C) | kJ/m2 |
ISO 179/1eA |
2.5 |
Ball indentation hardness ( H 358/30) |
MPa |
ISO 2039-1 |
70 |
Thermal Properties | |||
Melting point, DSC |
°C |
ISO 3146 |
163 |
Heat deflection temperature -------------- HDT/B ( 0.45 Mpa) |
°C |
ISO 75-2 |
85 |
Vicat softening temperature ---------------- VST/A50 (10 N) |
°C |
ISO 306 |
154 |
Other Properties | |||
Density | g / cm3 |
ISO 1183 |
0.91 |
* Provisional
Values given here are typical and should not be interpreted as specification. In a view of many factors that may affects processing
and application, these data do not relieve the receiver to this information from the responsibility of carry out their own test and experiments; neither do they imply any legally binding assurance of certain properties or of suitability for specific purpose of the product made
with or on the basis of the information in this publication.